Description
Description
- Application: During assembly, during break-in, and where continuous lubrication of parts exposed to high temperatures is required, suitable for dry lubrication of bearings (with low rotational speed), sliding guides, and joints exposed to temperatures exceeding +200°C. At higher temperatures, the carrier substance evaporates and leaves virtually no residue. The remaining dry sliding coating takes over lubrication up to +450°C and even at higher temperatures in a protective gas environment; the paste is suitable for lubricating structural components made of materials that are not resistant to mineral oils due to its synthetic oil base.
- Properties: Dry lubrication up to +450°C, reduction of friction and wear, low coefficient of friction, high load capacity, compatible with some types of natural rubber and plastics (compatibility tests must be conducted before use).
- Composition: polyalkylene glycol oil, lithium soap, solid lubricants
- Temperature range of use: from -40°C to +450°C, up to +630°C with restricted air access
- Packaging: tube: 50g; can: 1kg; barrel: 25kg
- Color: black
- Static penetration [mm/10]: 250 - 280
- Density at 20°C [g/ml]: 1.7
- Welding under load [N]: 3800 (Four-ball test)
- Wear value under load 800N/mm: 0.8 (Four-ball test)
- Pressfit test: 0.09
- Measurement of friction coefficient in screw connections: µ Thread: 0.14; µ Head: 0.12
- Water resistance at 90°C: 0