Description
Description
- Application: For combinations of metal/metal materials working at low to medium speeds and under high load. Suitable for long-term lubrication of highly stressed sliding guides with low or fluctuating sliding speeds or intermittent operation. Improves the break-in process and is suitable for lubrication in vacuum environments and extreme temperatures. Successfully used on fitted screws, toaster guides, in the mechanisms of automotive rearview mirrors, high voltage switches, during the break-in of highly stressed gears, standby lubricant for rotor head components in wind turbines, and is also used to achieve grooveless cold extrusion of steel.
- Examples of use: Lubrication of expansion friction surfaces on steel structures, Lubrication of fan blades in aircraft engines and Lubrication of the trigger mechanism of the Glock pistol including measuring trigger resistance before and after lubrication
- Properties: Air-curing, prevents stick-slip, high aging resistance.
- Composition: solid lubricants; inorganic binder; solvents
- Temperature range of use: from -180°C to +450°C
- Packaging: spray: 400ml; can: 1kg; barrel: 5kg
- Color: black-gray
- Solid lubricant particles: MoS2
- Solvents: organic
- Binder: inorganic
- Drying time at 20°C [min]: 5
- Curing [min/°C]: 5/+20
- Load capacity pressure Falex (surface was phosphated before application) [N]: 12500
- Vibrational corrosion Debyer test [oscillations]: 14 x 106
- Diluent: Molykote ® L 13 Thinner
- Flash point [°C]: +23